• NACE 96060428

NACE 96060428

  • Book by National Association of Corrosion Engineers,
  • Category: NACE

$24.00 $12.00

Slow strain rate tests (SSRT) were performed on a highpurity0.02% C steel in ammonium carbonate ([NH4]2CO3)solutions at 70°C as a function of applied electrochemicalpotential. As in previous studies, a narrow critical potentialrange for fatal cracking in the active-to-passive transition ofa rapidly developed polarization curve was observed. Atpotentials slightly active to the critical potential range,transgranular (TG) and intergranular (IG) fissuring wereobserved. At potentials noble to the critical range, IG fissuringwas observed. Fatigue precracking had no effect on theextent or rate of stress corrosion cracking (SCC), nor didhydrogen embrittlement (HE). Results supported previoustheories that IGSCC of carbon steels is the result of a veryspecific interaction between grain-boundary chemistry andthe micromechanics of near-boundary interactions.
PDF

All of our standards document are available in PDF (Portable Document Format), an electronic, downloadable format.You will be able to download the file in your account downloads.

Multi-User Access

After purchasing, you have the ability to assign each license to a specific user.

Printable

At any time, you are permitted to make printed copies for your and your members' reference use.

NACE TM0190-2006

NACE TM0190-2006

Standard Test Method - Impressed Current Test Method for Laboratory Testing of Aluminum Anodes..

$83.00 $166.00

NACE SP0387-2006

NACE SP0387-2006

Standard Practice - Metallurgical and Inspection Requirements for Cast Galvanic Anodes for Offshore ..

$79.00 $157.00

NACE 10A392

NACE 10A392

Effectiveness of Cathodic Protection on Thermally Insulated Underground Metallic Structures..

$17.00 $33.00

NACE No. 2/SSPC-SP 10

NACE No. 2/SSPC-SP 10

Joint Surface Preparation Standard: Near-White Metal Blast Cleaning..

$30.00 $59.00